POLYESTER  RESIN  IMPREGNATED

 GLASS  BANDING  TAPE

 

         福州佳为事进出口有限公司          Fuzhou Canwell Import & Export Co., Ltd.

         Tel: 0086-591-87610093 / 87614264 or 87279367 EXT.12                Rm. No. J, 21/F., Huakaifugui Building A,

         Fax: 0086-591-83640189 / 87279269                       No.36, Dongda Road, Fuzhou, China.

         H.P.: 0086-13509378762                      E-mail:qqmd@pub1.fz.fj.cn

Introduction:

SHU DA H200,F155 banding tapes are of high quality, which consist of parallel twisted E-glass yarns preimpregnated with a special thermosetting polyester resin.

SHU DA H200,F155 banding tapes ate manufactured with the proprietory technology and advaced equipments which are transferred form VONROLL ISOLA of ITALY.

SHU DA H200,F155 banding tapes ate widely used in AC,DC motors,generators and transformers especially in traction motors.

Specification

type	width (mm)	thick ness (mm)	put up
H200-W F155-W	10.15.20.25.30.50.60 ±10%	0.30 ±10%	spool or pancake

Properties

		H200-W	F155-W
Thermal class		H	F
Volatile contenf	%	not above: 2
Loss of  weight at calcination	%	26±2
Soluble resin content	%	above: 90
Tensile strength before curing	N/cm	above: 2000	above: 1000*
Maximum pull while banding	N/cm	1000	800
Tensile strength of ringlike sample at room temperature after curing	Mpa	20℃
		above: 1000	above: 900*
Tensile strength of ringlike sample at working temperature after curing	Mpa	200℃	155℃
		above: 700	above: 560*
Proof tracking index	S	above:500V
Are resistance		above:160
Breakdown voltage parallel to layers	KV	normal condition:               above:  25 after soaked in water for 24 hours:  above:  10
Thermosetting		OK
Loss of tensile strength after soakedin oil		not above: 10%

* The properties of F155-W ate partly according to Chinese standard of JB/T 6236.3-92 (2841-W)